C28000

C28000 is a lead-free material which is however quite suitable for machining Due to its structural constitution. C28000 can be therefore used as a cost-effective Replacement for conventional lead-containing machining brass provided that it must not meet high requirements as regards mechanical properties and corrosion Resistance

Chemical Composition

Elements	Min (%)	Max (%)
Cu	59.00	63.00
Pb	-	0.30
Fe	-	0.07
Total Others	-	0.30
Zn	Remainder

Mechanical Properties According To ASTM B36 (As Per Temper HO2)

Range (inch)		From	To	UTS Min (ksi)	UTS Max (ksi)	PS Min (ksi)	Elongation Min (%)	Hardness Min (HRB)	Hardness Max (HRB)
Round (Dia)		0.059	2.953	58	70	-	-	52	80
Hex (A/F)		0.118	2.756	58	70	-	-	52	80
Square (A/F)		0.118	2.362	58	70	-	-	52	80

Range (mm)		From	To	UTS Min (MPa)	UTS Max (MPa)	PS Min (MPa)	Elongation Min (%)	Hardness Min (HRB)	Hardness Max (HRB)
Round (Dia)		1.5	75	400	485	-	-	52	80
Hex (A/F)		3	70	400	485	-	-	52	80
Square (A/F)		3	60	400	485	-	-	52	80