C36500

Brass is essentially copper alloyed with zinc. It is strong but easy to form, stamp or draw which make it a common choice for a broad spectrum of applications. By varying the amount of zinc content it is possible to achieve a variety of characteristics including different levels of corrosion resistance, ductility and suitability for machining.

Chemical Composition

Elements	Min (%)	Max (%)
Cu	58.00	61.00
Pb	0.25	0.70
Fe	-	0.15
Total Others	-	0.40
Zn	Remainder

MECHANICAL PROPERTIES ACCORDING TO ASTM B981 (AS PER TEMPER HO2)

Range (inch)		From	To	UTS Min (ksi)	UTS Max (ksi)	PS Min (ksi)	Elongation Min (%)	Hardness Min	Hardness Max
Round (Dia)		0.059	0.500	63	-	28	10	-	-
		0.500	1.000	55	-	26	12	-	-
		1.000	2.000	48	-	24	20	-	-
		2.000	2.952	45	-	20	25	-	-
Hex (A/F)		0.118	0.500	63	-	28	10	-	-
		0.500	1.000	55	-	26	12	-	-
		1.000	2.000	48	-	20	25	-	-
		2.000	2.756	45	-	20	25	-	-
Square (A/F)		0.118	0.500	63	-	28	10	-	-
		0.500	1.000	55	-	26	12	-	-
		1.000	2.000	48	-	24	20	-	-
		2.000	2.362	45	-	20	25	-	-

Range (mm)		From	To	UTS Min (MPa)	UTS Max (MPa)	PS Min (MPa)	Elongation Min (%)	Hardness Min	Hardness Max
Round (Dia)		1.5	12	430	-	190	10	-	-
		12	25	380	-	180	12	-	-
		25	50	330	-	165	20	-	-
		50	75	310	-	135	25	-	-
Hex (A/F)		3	12	430	-	190	10	-	-
		12	25	380	-	180	12	-	-
		25	50	330	-	165	20	-	-
		50	70	310	-	135	25	-	-
Square (A/F)		3	12	430	-	190	10	-	-
		12	25	380	-	180	12	-	-
		25	50	330	-	165	20	-	-
		50	60	310	-	135	25	-	-